This study is concerned with the fabrication of engineering ceramics with complicated shapes by using the Slip Casting Process. In the previous report, we showed the conditions for preparing well-dispersed and high solid content Y-PSZ slurries. In this report, we will show the results of slip casting and sintering of Y-PSZ. High density green bodies, form 46 to 50% of the theoretical density, were obtained by the slip casting using well-dispersed and high solid content slurries of 3 kinds of starting powders. From high density green bodies, high density sintered bodies, above 99%, were obtained at the sintering conditions at 1500°C, 2h, in air for 3 kinds of starting powders. The bending strength for sintered bodies showed from 1 to 1.2GPa when the green bodies were sintered at from 1350 to 1500°C in air.